SCMT 120408-MM ET23P Carbide Medium Cutting Inserts Edgetech

£6.12

(Exc. 20% VAT)

~~£21.85~~

Save:

72%

In stock, immediate despatch

–

+

Part Number

TI01418

Shape

SCMT

Relief Angle

Positive = 7? (Screw on)

Edge Length

12 (12.4mm)

Thickness ISO/mm

04 (4.76mm)

Radius

08 (0.8mm)

Grade

ET23P

Chipbreaker Code

MM

Interrupted Cut?

No - Stable conditions

Will Cut Steel? (P-Blue)

No

Will Cut Stainless Steel? (M-Yellow)

Yes - Excellent

Will Cut Cast Iron? (K-Red)

No

Will Cut Heat Resistant Alloys? (S-Orange)

Yes

Will Cut Non-Ferrous? (N-Green)

No

Will Cut Hardened Steel? (H-Grey)

No

Information

ISO Designation	Edge Length LE (mm)	Thickness S (mm)	Radius RE(mm)	Chipbreaker	Grade
SCMT120408-MM	12 (12.7)	04 (4.76)	08 (0.8)	MM	ET23P

Grade: ET23P
Type: Single layer PVD coated grades are designed to balance edge strength with extended tool life..
Colour: Gold
Grade Summary: ET23P First choice for stable turning of Stainless Steel.
Type of Cut: MM chipbreaker - Medium cutting of stainless steels with stable/uninterrupted cuts.
Best for: Stainless Steels.

Technical Data & Info

Feed Rate & Depth of Cut

fn (mm/rev)	0.10 - 0.30
ap (mm)	0.6 - 4.0

Speeds Chart

Material VDI Group	Material Designation	Material Condition	Hardness	Grade	Speed M/Min
12	Stainless steel & Cast stainless steel	Ferritic/Martensitic, Annealed	≤200 HB	ET23P	110 - 180
13	Stainless steel & Cast stainless steel	Martensitic, Quenched & Tempered	≤240 HB	ET23P	110 - 180
14	Stainless steel & Cast stainless steel	Austenitic	≤180 HB	ET23P	40 - 130
31	Heat resistant super alloys	Fe based, Annealed	≤200 HB	ET23P	20 - 40
32	Heat resistant super alloys	Fe based, Aged	≤280 HB	ET23P	20 - 40
33	Heat resistant super alloys	Ni or Co based, Annealed	≤250 HB	ET23P	20 - 40
34	Heat resistant super alloys	Ni or Co based, Aged	≤350 HB	ET23P	20 - 40
35	Heat resistant super alloys	Ni or Co based, Cast	≤320 HB	ET23P	20 - 40
36	Titanium alloys	Pure Titanium	400 Rm	ET23P	20 - 40
37	Titanium alloys	Alpha & Beta alloys, Hardened	1050 Rm	ET23P	20 - 40